Synthetic primer based on vinylic copolymers, excellent anti corrosive power. Excellent covering properties. Excellent adhesion on iron and zinc plated sheets after treatment with mechanical devices or sanding

Water based primer for metalwork and other substrates, low odour and available in any colour.

Two-component epoxy-polyammide anticorrosive primer. Good anti-corrosive power. Good adhesion on treated zinc plated sheets (use Q120), iron after treatment with mechanical devices or sanding. It is also suitable as intermediate layer in anticorrosive cycles for iron structures.

Intermediate epoxy polyamide primer, high thickness of layers (200 micron each layer), good adhesion. Application at temperatures not lower than + 5/10 °C. after treatment of the structure with mechanical devices or sanding on iron and on zinc plated sheets. Overcoat after 1 hour with epoxy, polyurethane or acrylic enamels.

2K topcoat with excellent resistance to atmospheric agents and stability at light. Very good gloss and wholeness level. Because of the characteristics of the used raw materials, this product is recommended for valuable paintings mostly in industrial refinish, and steel work in general

Two-component polyurethane enamel with high gloss, water-proof, hardness, elasticity, excellent resistance to scratching. ISOPOL Z, because of its polyurethane nature, is suitable as anticorrosive for any kind of valuable industrial painting.

Semigloss 2K enamel with water-proof, hardness, elasticity, excellent resistance to scratching. ISOPOL ZS, because of its polyurethane nature, is suitable as anticorrosive for any kind of valuable industrial painting

Two-component polyurethane enamel based on modified polyester resins with matt appearance. Excellent resistance, stability to light, if catalized with aliphatic isocyanate. Very good resistance to abrasion, painting film is hard, elastic and water-proof. ISOPOL ZON, because of its polyurethane nature, is suitable as anticorrosive for any kind of valuable industrial painting

Glossy polyacrylic waterborne enamel with low organic solvent content (10-12%). Good fast drying, gloss and exellent weathering resistance. Apply 2 coats, the second one after 10 min the first one and without exceed 50/60µ dry to avoid the formation of craters, on perfectly dried waterborne or solventbase primer.

Matt polyacrylic waterborne enamel with low organic solvent content (10-12%). Good fast drying and exellent weathering resistance.

Metallic Finish Direct to Metal Paint. Ideal for most metalwork & can be applied by brush, roller or spray.

One-component top coat, based on modified acrylic resins. Fast drying. Good outdoor resistance. Good anti-corrosive property.

Monocomponent based on pheinilmetilsilicone resins that are modified with acrylic resins and with heat resistant pigments (till about 250°C excluded organic pigments). It is possible to apply directly on iron after treatment of the structure by degreasing or phosphation. 20 – 30 minutes baking at 80 – 100 °C is recommended.